As a follow up to my heatsink question, frame no2 will need a means to adjust chain tension. I could do this via an ebb rather than track ends (fixed dropouts might be advantageous) but would a larger diameter shell be more susceptible to distortion from brazing?
I could probably/possibly find cromo tubing of the requisite internal diameter with a heavier than normal wall thickness if that would help.